Product Name: 2A12 Aluminum Plate/Sheet
State: O, T3, T4, T351, H112
Payment Terms: L/C, T/T, PayPal, Western Union
Product Indroduction2A12 aluminum alloy is a high-strength hard aluminum, which can be strengthened by heat treatment;
2A12 aluminum alloy spot welding is good, with gas welding and argon arc welding, there is a tendency of intergranular crack formation; 2A12 aluminum alloy can be cut after cold hardening.
Product Specifications1. Width:500mm-1500mm
2. Length: according to your requirements
3. CE & ISO
Product Data
Chemical Composition | ||||||||||
Alloy |
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Zn |
Ti |
Al |
Others |
Max |
Max |
Max |
Max |
Max |
Max |
Max |
Max |
Min | ||
2A12 |
0. 5 |
0. 5 |
3.8-4.9 |
0.3-0.9 |
1.2-1.8 |
0.1
|
0.25 |
0.15 |
The Remaining |
0.15 |
Mechanical Properties | ||||
Aluminum Alloy & Temper |
Tensile Strength Rm/Mpa |
Proof Strength Rp0.2/Mpa |
Percentage Elongation After Fracture A/% |
Hardness HB |
2A12-T4 |
≥425 |
≥275 |
12 |
120 |
Mainly used to make various high load parts and components (but not including stamping parts forgings) such as aircraft skeleton parts, skin, bulkhead, fin, wing beam, rivets and other 150 ℃ working parts.
1. Standard Exporting package.
2. Original package or neutral package.
3. According to clients ' needs.
4. Shipped in10-35 days after payment.